This product code is IOTA 105-1000. The product function is mainly used as one-step synthesis raw material of different molecular weight epoxy silicone oil. The direct synthesis method has solvent-free, light color, crystal clear, simple process, convenient use and good reproducibility. And many other advantages.
Product introduction and application:
1, Appearance: light yellow transparent liquid
2, Molecular weight: M = 1000
3, Structural formula:
4, Characteristics:
Synthetic silicone oil does not require solvent, light color, crystal clear, simple process, convenient use and good reproducibility.
5. Epoxy silicone oil synthesis reference process:
a. Put D4, chain extender and catalyst alkali glue in the reaction vessel (the amount of catalyst is 0.6~1‰ of the total amount of synthesis), heat up to 105~110°C, keep warm for 3~3.5 hours, then raise the temperature to 140~150°C. , heat for 1 hour, and vacuum off at 140 ~ 150 ° C for 30 minutes, cooling, discharging.
b. If the catalyst is tetramethylammonium hydroxide solid, first put 1⁄3-1⁄4DMC and the total amount of catalyst (0.6~1‰), and then vacuum to 75-80 °C while heating, continue dehydration for half an hour until dehydration is completed, add The remaining DMC and IOTA 105-1000, then warmed to 105 ~ 110 ° C, heat for 3 ~ 3.5 hours, then warmed to 140 ~ 150 ° C, heat for 1 hour, and vacuum at 140 ~ 150 ° C for 30 minutes, cooling , discharge (from 3% to 5% of the total amount of monomer, not off).
6, Reference feeding ratio:
Molecular Weight
IOTA 105-1000
D4 or DMC Dosage
4000
100
330
6000
100
550
8000
100
770
10000
100
990
13000
100
1320
15000
100
1540
20000
100
2090
25000
100
2640
7, Instructions:
The above process and feeding ratio are for reference only, please adjust according to your actual situation.