Easy Processing and Excellent Performance

IOTA FHTV 3260 is an organosilicon compound. It is extremely easy to process. After adding an appropriate curing agent, it can be formed into the desired products through hot vulcanization. It boasts good mechanical properties, with high strength and resilience. This ensures that the products made from it are durable and reliable during use. Moreover, it exhibits excellent oil resistance, solvent resistance, and high - and low - temperature resistance. When exposed to transformer oil, it can maintain a relatively low dielectric loss, providing stable support for applications in the electrical field.

Detailed Technical Specifications

Looking at the product's technical specifications, each data point reflects its reliable quality. It has a semi - transparent appearance and a density of 1.43 g/cm³ (ASTM D792 standard). Its hardness is 60 shoreA (ASTM D2240 standard), with a tensile strength of 9.1 MPa (ASTM D412 standard), an elongation at break of 370% (ASTM D412 standard), and a tear strength of 19 KN/m (ASTM D624 - B standard). In terms of heat resistance, after a 200℃×72h test, the change in hardness (Shore A) is +3, the change rate of tensile strength is - 20%, and the elongation at break is - 21%. The volume change rate of Fuel C at 25℃/72h is +20% (ASTM D471 standard). Although these are typical performance data, they fully demonstrate the stability of the product's performance.

Processing Recommendations and Wide Applications

For processing, it is recommended to use 0.6 - 1 parts of 2,5 - dimethyl - 2,5 - bis(tert - butylperoxy)hexane as the curing agent. Customers should determine the most suitable vulcanization temperature and time according to the product size and vulcanization method. This product has a wide range of applications. It can be used for molded products, injection - molded products, and extruded tube - shaped products. No matter which molding method is used, it can fully exert its good mechanical properties to meet the needs of different fields.

Packaging and Storage

The product is packaged in 20 Kg per box, which is convenient for transportation and storage. When stored in its unopened original packaging at a temperature below 40℃, it can be kept for 12 months from the production date, providing convenience for long - term use.